Adornova P 200
Package á 25 g
High gold-containing bonding alloy
104,90 € excl. VAT
Description
>>> GebrAnw-Dental-Base-Alloy-Adornova-P-200.pdf <<<
| Type: | High-gold containing metal-ceramic alloy on the gold basis, type 4 (extra hard)
acc. DIN EN ISO 22674 |
| Colour: | yellow |
| Applicable scope: | Inlays, Onlays | |
| Crowns | ||
| Small bridges | ||
| Large-span bridges | ||
| Milling, cone and attachment works | ||
| Modeling casting |
| Composition: | Au | 84,40 |
| (mass fraction in %) | Pt | 8,00 |
| Pd | 5,00 | |
| Ir | 0,10 | |
| In | 2,50 |
| Technical specifications: | Density in g/cm³ | 18,2 |
| Vickers hardness HV 5/30 | (s)170 (n)200 (a-n)220 | |
| Yield strength Rp0,2 in MPa | (s)400 (n)450 (a-n)550 | |
| Elongation at break in % | (s)8 (n)7 (a-n)5 | |
| Average linear CTE 25 – 500 °C in 10-6 K-1 | 14,2 | |
| Average linear CTE 25 – 600 °C in 10-6 K-1 | 14,4 | |
| Elastic modulus in GPa | 95 | |
| Melting interval in °C | 1090 - 1210 |
| Processing: | Preheating temp. of the casting moulds in °C | 850 |
| Casting temperature in °C | 1360 | |
| Crucibles | Graphite | |
| Curing | 500°C/15min |
| Suitable solders: | Joints before ceramic firing | AuroCer Lot 1060 yellow |
| Joints after ceramic firing | AuroDur H Lot 750 |
1) Brief description:
s – self-curing, n – after ceramic firing, a-s – curing from s condition
a-n – curing from n condition
2) All information about cured condition is given according to the alloy:
– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys
– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys
– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems
Corresponding data are true under these conditions only.
3) The ceramic firing should be carried out according to the manufacturer's instructions.
Additional information
| Weight | 33 g |
|---|