ST WHITE Super Translucent White
Zircon blanks from Santa Barbara
for Monolithic restorations in the anterior and posterior region (crowns and bridges)
- Color: White
- Flexural strength 1200Mpa
- Translucency 43%
- Natural effect
- Lightweight and durable
- Biocompatible
- Low thermal conductivity
Also suitable for implant-supported crowns and bridges as well as implant prostheses
59,90 € – 99,90 € excl. VAT
| Menge | Preis/Stück |
|---|---|
| 5 - 9 | 56,91 € |
| 10 - 24 | 53,91 € |
| 25 - 49 | 50,92 € |
| 50 + | 47,92 € |
Description
Santa Barbara Super Translucent White Zirconia
is the high-strength, highly translucent monolayer solutioning for outstanding, natural looking
Results. It is supplied in white and can be to Demand colored become, so that one
variety of working solutions is possible. The high Bending strength (1200 MPa) enables
dauand safe restorations that are suitable for all types of processing are suitable.
Chemical composition and Technical specifications
|
ZrO₂+HfO₂+Y₂O₃ |
% | ≥ 99 | Density before sintering ϱ | g - cm-3 | 3,15 ± 0,05 | |
| Y₂O₃ | % | 4,5 – 6,0 | Density after sintering ϱ | g - cm-3 | 6,09 ± 0,01 | |
| Al₂O₃ | % | < 0,15 | Linear coefficient of thermal expansion α 25 - 500 °C | 10-6-K-1 | 10,5 ± 0,05 | |
| Other oxides | % | < 0,15 | ||||
| Flexural strength after sintering | MPa | 1200 | ||||
| Light transmission | % | 43 | ||||
| Cytotoxicity | Level 0 | |||||
| Radioactivity | Bq- g-1 | <0,1 | ||||
| Sintering temperature | °C | 1500 – 1550 | ||||
| Chemical solubility after sintering | µg- cm-2 | <100 | ||||
| Monoclinic phase content of the aging surface | % | 15 | ||||
Sintering curve
Additional information
| Weight | n.a. |
|---|---|
| Size | 98mm x 12mm, 98mm x 14mm, 98mm x 16mm, 98mm x 18mm, 98mm x 20mm |
Only logged in customers who have purchased this product may leave a review.
Reviews
There are no reviews yet.