ADORNOVA P 500
Package á 25 g
High gold-containing bonding alloy
97,90 € excl. VAT
Description
>>> GebrAnw-Dental-Base-Alloy-Adornova-P-500.pdf <<<
| Type: | High-gold containing metal-ceramic alloy on the gold basis, type 4 (extra hard), acc. DIN EN ISO 22674 |
| Colour: | yellow |
| Applicable scope: | Inlays, Onlays | ● |
| Crowns | ● | |
| Small bridges | ● | |
| Middle-sized bridges | ● | |
| Large-span bridges | ● | |
| Milling, cone and attachment works | ● | |
| Modeling casting | ● |
| Composition: | Au | 85,90 |
| (mass fraction in %) | Pt | 11,70 |
| Rh | 0,20 | |
| Ir | 0,05 | |
| Zn | 1,50 | |
| Nb | 0,40 | |
| Mn | 0,10 | |
| In | 0,10 | |
| Fe | 0,05 |
| Technical specifications: | Density in g/cm³ | 18,9 |
| Vickers hardness HV 5/30 | (s) 170 (n) 200 (a-n) 250 | |
| Yield strength Rp0,2 in MPa | (s) 440 (n) 490 (a-n) 620 | |
| Elongation at break in % | (s) 6 (n) 4 (a-n) 3 | |
| Average linear CTE 25 – 500 °C in 10-6 K-1 | 14,4 | |
| Average linear CTE 25 – 600 °C in 10-6 K-1 | 14,6 | |
| Elastic modulus in GPa | 95 | |
| Melting interval in °C | 1040 - 1130 |
| Processing: | Preheating temp. of the casting moulds in °C | 850 |
| Casting temperature in °C | 1280 | |
| Crucibles | Graphite | |
| Curing | 450°C/15min |
| Suitable solders: | Joints before ceramic firing | AL 1040 PF |
| Joints after ceramic firing | AL 750 |
1) Brief description:
s – self-curing, n – after ceramic firing, a-s – curing from s condition
a-n – curing from n condition
2) All information about cured condition is given according to the alloy:
– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys
– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys
– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems
Corresponding data are true under these conditions only.
3) The ceramic firing should be carried out according to the manufacturer's instructions.