3D-Pro-Multilayer
Zircon blanks from Santa Barbara
for monolithic Restorations in the Anterior and posterior teeth (crowns and bridges) as well as implant-supported crowns and bridges
-16 Vita colors
-5 Increasing resistance layers
(800 Mpa; 900 Mpa; 1000 Mpa; 1100
Mpa;1200 Mpa)
- Translucency 42% - 49%
-Natural effect
-Lightweight and durable
-Biocompatible
-Low thermal conductivity
139,90 € – 199,90 € excl. VAT
| Menge | Preis/Stück |
|---|---|
| 5 - 9 | 132,91 € |
| 10 - 24 | 125,91 € |
| 25 - 49 | 118,92 € |
| 50 + | 111,92 € |
Description
Santa Barbara 3D Pro Multilayer Zirconia
is the ideal solution to meet the required high aesthetic standard.
layers of different color, translucency and strength (from 800 to 1200 MPa) offer a wide range of
Spectrum of surgical options for the entire dental arch. Available in 16 colors and
different thicknesses for each application, which personalized, safe and natural
lookrestorations is required.
Chemical composition and Technical specifications
|
ZrO₂+HfO₂+Y₂O₃ |
% | ≥ 99 | Density before sintering ϱ | g - cm-3 | 3,1 ± 0,05 | |
| Y₂O₃ | % | 4,5 – 10 | Density after sintering ϱ | g - cm-3 | 6,07 ± 0,02 | |
| Al₂O₃ | % | < 0,15 | Linear coefficient of thermal expansion α 25 - 500 °C | 10-6-K-1 | 10,5 ± 0,05 | |
| Other oxides | % | < 0,5 | ||||
| Flexural strength after sintering | MPa | 800 – 1200 | ||||
| Light transmission | % | 42 -49 | ||||
| Cytotoxicity | Level 0 | |||||
| Radioactivity | Bq- g-1 | <0,1 | ||||
| Sintering temperature | °C | 1480 – 1530 | ||||
| Chemical solubility after sintering | µg- cm-2 | <100 | ||||
| Monoclinic phase content of the aging surface | % | 15 | ||||
Sintering curve
Additional information
| Weight | n.a. |
|---|---|
| Size | 98mm x 14mm, 98mm x 16mm, 98mm x 18mm, 98mm x 20mm |
| Colour | A1, A2, A3, A3.5, A4, B2, B3, C1, C2, C3, D2 |