ADORBOND 40

Description

>>> GebrAnw-Dental-Base-Alloy-Adorbond-40.pdf <<<

Type:	Gold-reduced metal-ceramic alloy on the gold basis, type 4 (extra hard) acc. DIN EN ISO 22674
Colour:	white

 

Applicable scope:	Inlays, Onlays	●
	Crowns	●
	Small bridges	●
	Large-span bridges	●
	Milling, cone and attachment works	●
	Modeling casting	●

 

Composition:	Au	40,00
(mass fraction in %)	Pd	39,40
	Ag	10,00
	In	8,80
	Ga	1,40
	Ru	0,10
	Sn	0,30

 

Technical specifications:	Density in g/cm³	12,2
	Vickers hardness HV 5/30	(s) 260 (n) 260 (a-n) 270
	Yield strength Rp0,2 in MPa	(s) 520 (n) 520 (a-n) 630
	Elongation at break in %	(s) 13 (n) 13 (a-n) 11
	Elastic modulus in GPa	120
	Average linear CTE 25 – 500 °C in 10-6 K-1	14,1
	Average linear CTE 25 – 600 °C in 10-6 K-1	14,4
	Melting interval in °C	1150 – 1270

 

Processing:	Preheating temp. of the casting moulds in °C	900
	Casting temperature in °C	1420
	Crucibles	Ceramic
	Curing	600°C/15min

 

Suitable solders:	Joints before ceramic firing	AL 1060 W
	Joints after ceramic firing	AL 750

 

1) Brief description:

s – self-curing, n – after ceramic firing, a-s – curing from s condition

a-n – curing from n condition

 

2) All information about cured condition is given according to the alloy:

– Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

– Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

– Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

Corresponding data are true under these conditions only.

 

3) The ceramic firing should be carried out according to the manufacturer's instructions.