Metallkeramiklegierung Adorbond S+

Adorbond S+

Package á 25 g

High gold-containing bonding alloy

 

104,90 € excl. VAT

Description

>>> GebrAnw-Dental-Base-Alloy-Adorbond-S+.pdf <<<

Type: High-gold containing metal-ceramic alloy on the gold basis, type 4 (extra hard) 

acc. DIN EN ISO 22674  
Colour: white
Applicable scope: Inlays, Onlays ●
Crowns ●
Small bridges ●
Large-span bridges ●
Milling, cone and attachment works 
Modeling casting ●
Composition: Au 77,20
(mass fraction in %) Pt 9,60
Pd 9,00
Ir 0,10
Ag 1,50
In 1,40
Sn 0,70
Cu 0,30
Fe 0,20
Technical specifications: Density in g/cm³ 17,6
Vickers hardness HV 5/30  (s) 170      (n) 200    (a-n)220
Yield strength Rp0,2 in MPa  (s) 380      (n) 440    (a-n)590
Elongation at break in %  (s) 7          (n) 8        (a-n)4
Average linear CTE 25 – 500 °C in 10-6 K-1 13,8
Average linear CTE 25 – 600 °C in 10-6 K-1 14,0 
Elastic modulus in GPa 110
Melting interval in °C 1170 - 1280
Processing: Preheating temp. of the casting moulds in °C 850
Casting temperature in °C 1430
Crucibles Graphite/ceramic
Curing 500°C/15min
Suitable solders: Joints before ceramic firing AL 1060 W
Joints after ceramic firing AL 750

1) Brief description: 

     s – self-curing, n – after ceramic firing, a-s – curing from s condition

     a-n – curing from n condition

2) All information about cured condition is given according to the alloy:

     – Oxide firing 10min/ 960°C + 4x4min/ 960°C for yellow conventional bonding alloys

     – Oxide firing 10min/ 980°C + 4x4min/ 980°C for white conventional bonding alloys

     – Oxide firing 10min/ 800°C + 4x4min/ 800°C for LFC-systems

   Corresponding data are true under these conditions only.

3) The ceramic firing should be carried out according to the manufacturer's instructions.